Abstract

Phase equilibria in the Ti-Nb-Mn ternary system at 1173K, 1273K and 1373K were studied through the equilibrated alloy method by using scanning electron microscopy (SEM), electron probe microanalysis (EPMA) and X-ray diffraction (XRD) techniques. A new stable ternary phase K was confirmed and the composition was around Ti50Nb7Mn43. A wide-range continuous solid solution phase (Ti,Nb)Mn2 with the C14 Laves structure had been found at these temperatures due to the same phase structures of TiMn2 and NbMn2 phases. The solubility of Nb in TiMn4, αTiMn and βTiMn intermetallic compounds was determined. Based on the experimental results and reasonable extrapolations, the isothermal sections of Ti-Nb-Mn ternary system at 1173K, 1273K and 1373K were constructed.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.