Abstract
The V-rich part of the Al–Si–V phase diagram was determined by a combination of optical microscopy, powder X-ray diffraction (XRD), differential thermal analysis (DTA) and electron probe microanalysis (EPMA). Phase equilibria were investigated at two isothermal sections at 850 and 1300 °C. High temperature DTA was performed to identify the ternary invariant reactions yielding a ternary reaction scheme and the vertical section at 50 at.% V. As cast samples were investigated in order to gain additional information about primary crystallization fields. A liquidus surface projection was constructed for the entire ternary system by combining our experimental data with those from literature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.