Phase equilibria in the Al–Mo–Si system

Abstract

The ternary Al–Mo–Si phase diagram was investigated by a combination of optical microscopy, powder X-ray diffraction (XRD), differential thermal analysis (DTA), electron probe microanalysis (EPMA) and scanning electron microscopy (SEM). Ternary phase equilibria were investigated within two isothermal sections at 600 °C for the Mo-poor part and 1400 °C for the Mo-rich part of the phase diagram. The solubility ranges of several phases including MoSi 2 (C11 b) as well as Mo(Si,Al) 2 with C40 and C54 structure were determined. The binary high temperature phase Al 4Mo was found to be stabilized at 600 °C by addition of Si. DTA was used to identify 9 invariant reactions and thus constructing a ternary reaction scheme (Scheil diagram) in the whole composition range. A liquidus surface projection was constructed on basis of the reaction scheme in combination with data for primary crystallization from as-cast samples determined by SEM measurements.