Abstract
Phase equilibria and stabilities of intermetallic phases appearing in the Co-rich portion of the Co-W-Ga ternary alloys were investigated and isothermal section diagrams at 1200, 1100, 1000, and 900 °C were determined. A fine cuboidal phase with an L12 structure was observed at 900 and 800 °C, where the composition of the new ternary compound obtained by aging at 900 °C for the Co-7.4W-12.0Ga alloy was Co-11.2W-11.4Ga (at.%). It was confirmed that this compound is metastable at 900 °C but is more stable at 800 °C. These results mean that the thermodynamic stability of the metastable Co3W L12 phase, especially in the low temperature region, increases by the addition of Ga.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.