Abstract
AM samples both in as-deposited and heat-treated states have been subjected to microstructural and phase characterization. Mechanical testing has been performed to heat-treated samples with respect to the build directions. AM samples were made by Direct Laser Deposition under the three different levels of efficient energy from Inconel 718 powder. As-deposited samples contained dispersed particles of Fe2Ti Laves phase, NbC and NbNC as well as starting clusters of γ′ phase. Although the standard heat treatment at 980 °C was found to result in partial dissolution of Laves phase precipitation of δ phase occurred around it. Depletion in Nb of Ni-based matrix due to formation of NbC, NbNC and Laves phase in as-deposited states causes precipitation of γ′ phase as the main strengthening phase in heat-treated states. Fatigue crack propagation manners were analyzed with fractography. Fine columnar dendrite structure of samples tested in parallel build direction to the loading is much more resistant to fatigue crack propagation. Fatigue crack bypass dispersed Laves phase which is fixed in matrix by δ phase.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call