Thermodynamic phase behavior of poly(ε-caprolactone)-b-poly(tert-butyl acrylate) (PCL-b-PtBA) block copolymers at the Air/Water (A/W) interface was studied by analyzing surface pressure-area isotherms. Optical microscopy and atomic force microscopy were utilized to reveal the morphological features of three-dimensional domains grown in the Langmuir films. A series of PCL-b-PtBA block copolymers synthesized for this study share the same PCL block with molecular weight of Mn = 7.5 kg•mol−1, while the length of PtBA blocks varies. Homogeneous Langmuir monolayers were formed at the A/W interface before reaching the dynamic collapse pressure of PCL blocks. The growth of PCL flat-on crystalline domains predominately took place during the plateau regime after the collapse transition, though nucleation process occurred prior to the collapse transition. The tethered PtBA blocks remain as a monolayer at the A/W interface prior to the second collapse pressure at ∼ 24 mN•m−1, which is comparable to the collapse pressure of PtBA homopolymer monolayer. Depending on the length of PtBA blocks, the block copolymer crystals exhibit morphological features from distorted hexagonal shape, truncated parallelogram, dendrites with defects, stripes, and nano-scale domains, suggesting that the tethered amorphous PtBA block significantly reduced the mobility and packing efficiency of PCL blocks during the crystallization of PCL-b-PtBA copolymers at the A/W interface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Colloids and Surfaces A: Physicochemical and Engineering Aspects
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.