Abstract
The phase and morphology of precipitates in heat-treated Co-28Cr-6Mo-xC (x = 0.12, 0.15, 0.25, and 0.35mass%) alloys were investigated. The as-cast alloys were solution-treated in the temperature range of 1473 to 1623 K for 0 to 43.2 ks. Complete precipitate dissolution was observed in all four alloys, each of which had different carbon contents. The holding time for complete dissolution was greater for alloys with greater carbon content. The curve representing the boundary between the complete- and incomplete-dissolution conditions for each alloy is C shaped. Under the incomplete precipitate dissolution conditions of the Co-28Cr-6Mo-0.25C alloy, an M23C6 type carbide and a π-phase (M2T3X type carbide with β-Mn structure) were observed at 1548 to 1623 K, and starlike precipitates with a stripe pattern and with a dense appearance were both observed; the former comprised the M23C6 type carbide + γ-phase, and the latter was the π-phase. In contrast, only a blocky-dense M23C6 type carbide was observed at 1473 to 1523 K.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.