The phases formed in the wide-gap region brazed with Ni-14Cr-10Co-3.5Al-2.5Ta-2.8B filler metal powder in IN738 superalloy were investigated by electron backscatter diffraction (EBSD). The wide-gap brazing process was carried out in a vacuum of 2×10-5 torr at 1503 K. The region brazed with filler metal powders had a microstructure consisting of two kinds of eutectic colonies, one is Ni solid solution-CrB eutectic and the other is Ni solid solution-Ni3B eutectic. EBSD pattern analysis revealed that the CrB phase had orthorhombic structure with lattice parameters of a=0.297, b=0.786 and c=0.293 nm, and the Ni3B phase had orthorhombic structure with lattice parameters of a=0.439, b=0.522 and c=0.662 nm. The cuboidal-shaped phase precipitated in the Ni solid solution was found to be the γ' (Ni3Al) phase, which had cubic structure with lattice parameter of a=0.357 nm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.