Abstract
Through a simple hydrothermal and thermal decomposition process of the ammonium aluminum carbonate hydroxide (denoted as AACH) precursors, we prepared mesoporous γ-Al2O3 fibers with tunable diameters by manipulating the amount of urea (pH-adjuster) in the reaction mixture (i.e., pH control). The experimental results show that the diameter of the obtained AACH fibers decreased obviously when the pH values of the reaction mixtures changed from 2.5 to 5.0. The as-formed precursors could transform to the morphology-remained cubic γ-Al2O3 with a slight shrinkage in diameter of the fibers after an annealing process. N2 adsorption–desorption experiment indicates that the as-synthesized alumina microfibers and nanofibers have large surface area (176 and 230m2/g, respectively) and narrow pore-size distributions. Both the γ-Al2O3 microfibers and nanofibers are powerful in the removal of Congo red pollutant from waste water.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.