Permeability and corrosion resistance of porous SiOC‐bonded SiC ceramics prepared by the preceramic polymer

Abstract

AbstractPorous SiC ceramics have been used in high temperature flue gas filtration fields because of their excellent properties such as high strength, high temperature resistance, corrosion resistance, and long service time. This work reports the porous SiOC‐bonded SiC ceramics prepared at low temperature. The properties of porous SiC ceramics were first investigated with silicone resin content from 10 to 25 wt%, and then the effects of different pore‐forming agent contents on the behaviors of porous SiC ceramics were discussed by adjusting poly (methyl methacrylate) PMMA microbeads from 5 to 20 wt%. The prepared porous SiC ceramics showed apparent porosity from 17.3% to 57.7%, compressive strength from 6 to 216 MPa, and Darcy permeability k1 ranging from 7.02 × 10−14 to 1.45 × 10−12 m2. The corrosion behavior of porous SiC ceramics was investigated in acidic and alkaline media. The porous SiC ceramics showed better corrosion resistance in acidic solutions.