Abstract
Specimens were prepared using iron-rich magnesia (3~1 mm、≤1 mm) and high purity magnesia (≤0.088 mm) as the main starting materials, adding tabular alumina at different size (3~2、2~1、≤1 mm) and content:3%、6%、9%、12%、15% to discover the influence of tabular alumina on sample performance. Phase composition and microstructure were also analyzed. The results show that specimen with content of 6% of corundum possessed the best comprehensive performance:apparent porosity 17%, bulk density 2.95 g·cm-3, cold crushing strength 74 MPa, refractoriness under load 1700 °C, heat shock resistance of up to 18 times. The formations of magnesium aluminate spinel and hercynite solid solution were enhanced by Fe ion at high temperatures in the iron-rich magnesia-corundum system at the presence of iron oxides, which are able to largely dissolved in periclase.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.