Abstract
In this study, precursor solutions of La0.4Sr0.6Co0.2Fe0.7Nb0.1O3-δ (LSCFN) symmetric electrode were prepared, and the applications of cathode impregnation and full cell impregnation in the preparation and performance optimization of four-layer metal-supported solid oxide fuel cells (MSCs) were thoroughly investigated. Test results indicate that the polarization impedance of cathode impregnated MSCs under H2 and CH4 atmospheres at 750 °C is approximately 0.1 Ω cm2 and 0.41 Ω cm2, respectively, with power densities of 1115 mW cm-2 and 700 mW cm-2, respectively. Meanwhile, the polarization impedance of full cell impregnated MSCs under the same conditions is 0.12 Ω cm2 and 0.40 Ω cm2, with power densities of 945 mW cm-2 and 840 mW cm-2, respectively. Remarkably, MSCs full cell impregnated LSCFN exhibit outstanding stability performance under CH4 atmosphere in a 100 h stability test. Research on the application of impregnation method for performance optimization of metal-supported cells is relatively scarce. The results reveal the feasibility of simplifying MSCs preparation steps using full cell impregnation method, further promoting the widespread application of metal-supported overall cells.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.