Performance of novel hydroxyapatite nanowires in treatment of fluoride contaminated water

Abstract

Novel ultralong hydroxyapatite (HAP) nanowires were successfully prepared for fluoride removal for the first time. The fluoride adsorption on the HAP nanowires was studied on a batch mode. The results revealed that the adsorption data could be well described by the Freundlich model, and the adsorption kinetic followed the pseudo-second-order model. The maximum of adsorption capacity was 40.65mg/g at pH 7.0 when the fluoride concentration is 200mg/L. The thermodynamic parameters suggested that the adsorption of fluoride was a spontaneous endothermic process. The FT-IR, XPS and Zeta potential analysis revealed that both anion exchange and electrostatic interactions were involved in the adsorption of fluoride. Furthermore, the HAP nanowires were made into HAP membrane through a simple process of suction filtration. Membrane filtration experiments revealed that the fluoride removal capabilities depended on the membrane thickness, flow rate and initial concentration of fluoride. The as-prepared membrane could remove fluoride efficiently through continues filtration. The filtered water amount could reach 350, 192, and 64L/m2 when the fluoride concentrations were 4, 5 and 8ppm, respectively, using the HAP membrane with only 150μm thickness. The as-synthesized ultralong HAP nanowires were thus demonstrated to be very effective and biocompatible adsorbents for fluoride removal from contaminated water.