Abstract
Machining quality and productivity of superalloys are limited due to their poor machinability, and fewer studies have focused on the cutting of iron-based superalloys. In this study, the cutting performance of coated and uncoated carbide tools in high-speed dry turning iron-based superalloy GH2132 was investigated by performing a series of cutting experiments. The experimental results indicated that cutting temperature and cutting forces increased, while tool life decreased with the increase in the cutting speed from 30 to 100 m/min. Under relatively low cutting speeds, flank face wear was dominated by abrasion and adhesion, while rake face wear mainly involved built-up edge (BUE), built-up layer (BUL), adhesion, and breakage near the depth of cut. Under higher cutting speed, adhesion wear was more serious on the flank face, and peeling off of the coatings and substrate occurred on the rake face. Owing to the protective effect of (Ti, Al)N + TiN coating, the coated tools exhibited better wear resistance and thus longer tool life, in particular, under higher cutting speeds. Analysis of the tool wear gap in the horizontal direction indicates that better dimensional accuracy could be obtained when coated tools are used. In dry turning of GH2132 with carbide tools, a favorable surface finish could be obtained. The surface roughness roughly showed a tendency to first decrease and then increase with the increase in average flank wear. The coated tools should be avoided to machine GH2132 at higher cutting speed due to the poor surface finish.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Proceedings of the Institution of Mechanical Engineers, Part B: Journal of Engineering Manufacture
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.