Abstract
This research investigates the possibility of using high-density polyethylene (HDPE) plastic waste to improve the properties of asphalt concrete pavement. HDPE plastic waste contents of 1, 3, 5, and 7% by aggregate weight were used. HDPE plastic waste=stabilized asphalt concrete pavement (HDPE-ACP) was evaluated by performance testing for stability, indirect tensile strength, resilient modulus (MR), and indirect tensile fatigue (ITF). In addition, microstructure, pavement age, and CO2 emissions savings analyses were conducted. The performance test results of the HDPE-ACP were better than those without HDPE plastic waste. The optimum HDPE plastic waste content was 5%, offering the maximum MR, ITF, and pavement age. Scanning electron microscope images showed that the excessive HDPE plastic waste content of 7% caused a surface rupture of the sample. Improvements in the pavement age of the HDPE-ACP samples were observed compared with the samples with no HDPE plastic waste. The highest pavement age of the HDPE-ACP sample was found at an HDPE plastic waste content of 5% by aggregate weight. The CO2 emissions savings of the sample was 67.85 kg CO2-e/m3 at the optimum HDPE plastic waste content.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.