One kind of PVA/PAA-based alkaline solid polyelectrolyte (ASPE) membrane with high conductivity and good mechanical property was prepared via the introduction of the micro-crystalline cellulose (MCC) as functional fillers. An ion conductivity of 95 mS cm−1 with high alkali resistance was achieved when the MCC content reached up to 5wt%, which is 4.5-fold higher than the control. SEM image showed a denser pore structure that is beneficial for the OH− conduction after MCC addition. X-ray diffraction further indicated a gradually decreased crystallinity of KOH with the addition of MCC. This means more content of KOH would exist in the ionic form in the remained water caused by the added MCC in the system. This leads to the increased content of OH− and the resulting ion conductivity. The window equals to 0.9 V and improved mechanical properties were observed after a 5wt% content of MCC was added in the ASPE membrane system.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.