Abstract
Cement mortar is known to be effective in taking compression than tension. The tensile strength of cement mortar is a cause of concern when it comes to unreinforced applications. The present study aims at performance evaluation of Polyurethane (PU) and Nano silica blended cement mortar. Various proportion of polyurethane (0.5%, 1%, 2%) modified with nano silica (5%, 10% by weight of PU) is blended to the mix during specimen preparation. The water-cement ratio is maintained at 0.35 and the superplasticizer dosage maintained at 0.2% weight of cement. The performance study such as compressive strength, split tensile strength, resistance to thermal exposure, abrasion resistance was done. The relative assessment was also done with cement mortars incorporating silica fume (5% by weight of cement). Compared to cement and silica fume incorporated mortar, the mixes modified with PU-nano silica shows enhancement in split tensile strength. PU-nano silica composite also shows improvement in durability properties. XRD characterization was also performed on the composite mortar to identify the compounds present.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.