Pengaruh Variasi Kuat Arus Listrik dan Waktu Electroplating Nickel-Chrome terhadap Ketebalan Lapisan pada Permukaan Baja Karbon Rendah

Heribertus Sukarjo,R Soelarso Pani

doi:10.30588/jeemm.v2i1.355

Heribertus Sukarjo, R Soelarso Pani

Open Access

https://doi.org/10.30588/jeemm.v2i1.355

Copy DOI

Abstract

The development and progress of science and technology in the metal plating industry has become a field of work that is experiencing rapid advances ranging from the type of coating, a coating material that is used, and the results of a layer. The metal plating industry needs not only demand resistance to corrosion, but also the strength of the material, has a beautiful appearance, and has a high economic value. one of them, namely by means of electroplating coating. The purpose of this research is to know the influence of variations in the strength of an electric current and time of electroplating nickel-chrome against the thickness of the surface layer of low carbon steel. The benefits of this research are expected to add to the knowledge about the coating on the process of electroplating nickel-chrome and can apply it. In the activities of this research material used is low carbon steel plates with a size 40 mm x 25 mm x 1 mm with the number 27 specimens are coated using electroplating method with the variation of strength of electric current of 0.5 A, 1 A, 1.5 A and time electroplating 10 minutes, 15 minutes, 20 minutes. Testing done next the thickness of the layer. Results of the study showed that the highest hardness of nickel-chrome electroplating process occurs on a variation of value the highest layer thickness variation in the strength of the current 1.5 A long coating 20 minutes 1.97 µm.

Highlights

Perkembangan dan kemajuan ilmu pengetahuan serta teknologi pada industri pelapisan logam telah menjadi bidang pekerjaan yang mengalami kemajuan yang sangat pesat mulai dari jenis pelapisan, bahan pelapis yang digunakan, hingga hasil lapisannya
The development and progress of science and technology in the metal plating industry has become a field of work that is experiencing rapid advances ranging from the type of coating, a coating material that is used, and the results of lapisannya
The purpose of this research is to know the influence of variations in the strength of an electric current and time of electroplating nickel – chrome against the thickness of the surface layer of low carbon steel

Summary

PENDAHULUAN

Perkembangan dan kemajuan ilmu pengetahuan serta teknologi pada industri pelapisan logam telah menjadi bidang pekerjaan yang mengalami kemajuan yang sangat pesat mulai dari jenis pelapisan, bahan pelapis yang digunakan, hingga hasil lapisannya. Tersedianya material logam yang mempunyai keunggulan sangat diperlukan untuk menjadi bahan dasar dari komponen pelapisan logam. Kebutuhan industri pelapisan logam tidak hanya menuntut ketahanan terhadap korosi, namun juga kekuatan dari material, memiliki penampilan yang indah, serta memiliki nilai ekonomis yang tinggi. Beberapa macam pelapisan dapat digunakan untuk mencegah atau memperlambat tingkat kerusakan serta meningkatkan kekuatan mekanis logam tersebut, salah satunya yaitu dengan cara pelapisan electroplating (Deviana, 2014). Selain itu juga melindungi logam dasar dari korosi baik itu melindungi dengan logam yang lebih mulia seperti pelapisan platina, emas dan baja atau melindungi dengan logam dasar yang kurang mulia seperti pelapisan seng pada baja dan terakhir adalah meningkatkan ketahanan produk. E-ISSN 2579-7433 terhadap gesekan (abrasi), misalnya pelapisan chromium keras