Abstract
The studies, observation of microstructure and magnetic coercivity of the permanent magnet sample have been done through a metallurgy powders technique preparation process. The raw materials with the composition of Sm (Co, Cu, Fe, Zr)z equal 8.5 (at percent) initially in the form of powders alloys with the mean particle size of was 20-30 um. This powder is compacted through one direction pressed in the dies and the following with heat treatment steps. After sintering steps and homogeneity of each at a temperatures of 1190 degree celcius and 1130 degree celcius, the solid sample achieved with Sm2Co17 is mainly the magnetics phase. Further heat treatment that their received the next 10 degree celcius/minute until room temperature. And have succeeded to form cellular structures on the matrixs of magnetics phases while other phases in the form cellular structures on the matrixs of magnetics phases while other phases in the form of grain boundary and the magnetics coercivity. Conclution from result of this study is compared with the result of former research. Keywords: Magnet permanen, SmCo, Proses sintering, Struktur mikro, Koersivitas.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.