Abstract
Pd xNi y/C catalysts with high ethanol oxidation reaction (EOR) activity in alkaline solution have been prepared through a solution phase-based nanocapsule method. XRD and TEM show Pd xNi y nanoparticles with a small average diameter (2.4–3.2 nm) and narrow size distribution (1–6 nm) were homogeneously dispersed on carbon black XC-72 support. The EOR onset potential on Pd 4Ni 5/C (−801 mV vs. Hg/HgO) was observed shifted 180 mV more negative than that of Pd/C. Its exchange current density was 33 times higher than that of Pd/C (41.3 × 10 −7 A/cm 2 vs. 1.24 × 10 −7 A/cm 2). After a 10,000-s chronoamperometry test at −0.5 V ( vs Hg/HgO), the EOR mass activity of Pd 2Ni 3/C survived at 1.71 mA/mg, while that of Pd/C had dropped to 0, indicating Pd xNi y/C catalysts have a better ’detoxification’ ability for EOR than Pd/C. We propose that surface Ni could promote refreshing Pd active sites, thus enhancing the overall ethanol oxidation kinetics. The nanocapsule method is able to not only control over the diameter and size distribution of Pd–Ni particles, but also facilitate the formation of more efficient contacts between Pd and Ni on the catalyst surface, which is the key to improving the EOR activity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.