Abstract
Pb(Zr/sub 0.52/Ti/sub 0.48/)O₃(PZT) thin films were deposited by using a pulsed laser deposition method on a Pt/Ti/SiO₂/Si substrate with (Pb/sub 0.72/La/sub 0.28/)Ti/sub 0.93/O₃ (PLT) buffer and on a Pt/Ti/SiO₂/Si substrate without buffer. These films were annealed in H₂-contained ambient for 30 minutes at the substrate temperature of 400。C to evaluate the forming gas annealing effects. The comparative studies on the ferroelectric properties of these two films were carried out, which are shown that ferroelectric properties, such as remanent polarization didn't change in the case of PLT buffered PZT film while remanent polarization value of PZT film degraded from 20.8 C/㎠ to 7.3 C/㎠. The leakage current became higher in both cases, but that of the more-oriented PZT film had the moderate value of the 10/sup -6/ order of A/㎠. This is mainly because the hydrogen atoms which make the degradation of PZT films cannot infiltrate into the more -oriented PZT film as well as the less-oriented PZT film.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Korean Institute of Electrical and Electronic Material Engineers
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.