Abstract
Passivity of duplex stainless steel was studied after long-term ageing in air using local electrochemical impedance spectroscopy, AES, XPS and EBSD. After mechanical polishing, the passive film was homogeneous and had a capacitive behaviour described by the CPE. After long-term ageing, a small thickening was detected and O2−/OH− was significantly higher in the austenite than in the ferrite. Austenite behaved as a blocking electrode whereas two capacitive loops were observed in the ferrite (low value of O2−/OH). The loop at high frequencies was related with the oxygen reduction and the loop at low frequencies was connected with the passive film.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.