Abstract
In this study, nanocrystalline NiAl intermetallic compound was obtained by mechanical alloying and PAS (plasma activated sintering method). Nanocrystalline NiAl powder was fabricated after 30 hr of milling with 2 wt.% stearic acid added as a PCA (process control agent) to the Ni-50at%Al composition. The grain size of the nanocrystalline NiAl powder was about 10 nm. Nanocrystalline NiAl powder was consolidated at 1000°C, 1100°C, 1200°C and 1300°C for 2 min with 30 MPa compressive force. The surface morphology of the NiAl consolidated at 1300°C was very regular and dense, above 96% of theoretical density (5.9 g/cm3). Al4C3 was observed in the NiAl consolidated at 1300°C by TEM analysis. It is thought that the carbons came from the stearic acid during the MA process and the graphite mold during the PAS process. The grain size of the NiAl consolidated at 1300°C did not increase but the grain shape became flat due to compressive force.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.