Particle size reduction of RDX by sequential application of solvent–antisolvent recrystallization and mechanical methods

Abstract

ABSTRACT Solvent–antisolvent recrystallization produced ~8 µm average size RDX particles (UF-RDX) that were subsequently subjected to mechanical methods of ultrasonication and ball-milling to find further achievable reduction in particle size. Long duration ultrasonication for 20 h and 300 rpm ball milling for 4 h of UF-RDX decreased its average particle size to ~2 µm. RDX produced by all the three processes (solvent–antisolvent recrystallization, ultrasonication and ball-milling) was similar to coarser RDX in structure and thermal decomposition behavior. However, UF-RDX produced by solvent–antisolvent recrystallization was significantly less impact sensitive than that produced by ball-milling and ultrasonication. The issues of residual solvent and the metal contamination during RDX processing were addressed by process parameter optimization. Solvent–antisolvent recrystallization and mechanical methods even when used sequentially could not bring average particle size of RDX to nano-scale.