Abstract
Al-Al3Zr and Al-Al3Ti functionally graded materials (FGMs) were produced by a centrifugal method from Al-5wt% Zr and Al-5wt% Ti alloys, respectively. Applied centrifugal forces were 30, 60 and 120G (units of gravity). Microstructural characterization was performed to evaluate the intermetallic particles’ distribution and orientation. Knoop hardness tests were carried out, with the indenter’s long diameter normal to the centrifugal force direction. Both the Al3Zr and the Al3Ti intermetallic particles are platelet in morphology. These platelets tend to be oriented normal to the centrifugal force direction. Higher applied centrifugal force increases both the intermetallic platelet volume fraction as well as their orientation in the outer regions of the fabricated FGM rings. Also higher orientation and volume fraction distribution are observed in the Al- Al3Ti FGMs. Knoop hardness measurements in general follow the same trend as the intermetallic particle volume fraction for each sample.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.