Abstract
Two quanternary systems, Ir-Nb-Ni-Al and Ir-Nb-Pt-Al, were successively investigated to assess their possible use in ultra-high-temperature applications. The phase relationships concentrated on the fcc/L12 two-phase region were primarily established, and the mechanical properties were studied. Ir-Nb-Ni-Al quaternary alloys around the Ir-rich or Ni-rich corners of the Ir-Nb-Ni-Al tetrahedron showed a coherent fcc/L12 two-phase structure, analogous to that of Ni-base superalloys; however, most of the alloys presented three or four phases with two types of L12 phases. Although these alloys showed a high compressive strength at high temperature, they exhibited a higher creep rate than Ir-base binary and ternary alloys. Another quanternary system, Ir-Nb-Pt-Al, showed promising results. Only an fcc/L12 two-phase structure was found in all the alloys investigated with compositions ranging from the Ir-rich side to the Pt-rich side, and the lattice misfit between the fcc and L12 phases was small. The high-temperature strength at 1200 °C of Ir-Nb-Pt-Al alloys was higher than that of Ir-Nb-Ni-Al alloys with the same Ir content (at. pct). Moreover, Ir-Nb-Pt-Al alloys exhibited excellent creep resistance at 1400 °C and 100 MPa.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.