Abstract
A series of reheating-isothermal holding experiments and compression tests were conducted on pristine magnesium alloy AZ91 extruded by equal channel angular extrusion (ECAE) and SiC particles (a volume fraction of 15%) reinforced AZ91 composite (AZ91-SiCp) by regular extrusion. Dissolution of eutectic compounds and partial melting of the α-Mg matrix occurred during the reheating of these materials. Spherical semisolid slurries of these materials were obtained when the reheating temperature and isothermal holding time were 550°C and 20s, respectively. The presence of SiCp in AZ91-SiCp not only caused lower liquid fractions of semisolid slurries but also resulted in higher values of flow stress during semisolid compression tests. Both AZ91 alloy and AZ91-SiCp composite exhibited better thixoforming properties at high temperatures. Segregation of SiCp did not occur during thixoforming of AZ91-SiCp composite after an isothermal holding at semisolid temperatures for 20s.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.