Abstract
A TRIP-aided bainitic-ferritic (TBF) steel with a chemical composition of Fe–0.19C–1.7Mn–1.09Si–0.51Al–0.05Nb (wt-%) was partially austenitised from a hot-rolled martensitic initial microstructure. After the hot rolling, the martensitic specimens were reheated to different intercritical temperatures and then austempered at 350°C. Thus, the effect of the initial microstructure of TBF steel on intercritical austenite formation during partial austenitisation was studied. The microstructures were investigated by scanning electron microscopy and electron backscatter diffraction (EBSD), and the tensile properties were tested. Microstructural observations revealed that a final microstructure of fine ferrite, bainitic ferrite, and retained austenite can be obtained. The steel partial austenitised at 770°C showed a good combination of ultimate tensile strength and total elongation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.