Abstract
Thin film transistors (TFTs) with amorphous zinc tin oxide (ZTO) channel layer were fabricated by a simple and low-cost solution process, prepared by dissolving 0.2 M of zinc acetate dihydrate and tin chloride dihydrate in 20 mL of 2-methoxyethanol. All ZTO thin films showed amorphous phases and no impurities (no carbon and chlorine content) even at process temperature of 350 °C. As the Sn ratio in ZTO films increased, the values of saturated mobility (usat) and subthreshold gate swing (SS) exhibited a parabolic behavior in ZTO TFTs, depicting that the μsat and SS values were a maximum (3.4 cm2/V.s) and minimum (0.38 V/decade) at Zn/Sn = 1 ratio. Interestingly, the x-ray absorption and X-ray photoemission spectroscopy revealed the origin of parabolic behavior, indicating not only to improve a charge transport in conduction bands but also to increase the Sn4+/Sn2+ ratio at the peak values (Sn/(Zn + Sn) = 1).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.