Abstract
Effects of Yb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> fine dopant (16 nm) on the acoustic properties of a high-temperature-vulcanization (HTV) silicone rubber have been investigated, in order to develop a new acoustic lens material with a low acoustic attenuation (alpha) for the medical array probe application. The HTV silicone rubber has advantages in that it shows a lower alpha than that of a room-temperature-vulcanization (RTV) silicone rubber and it can be mixed by applying shear stress, using roll-milling equipment. Roll-milling time dependence of the HTV silicone rubber indicates that the alpha is closely affected by the dispersion of nanopowders in the rubber matrix. The 8 vol% Yb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> doped HTV silicone rubber mixed for 30 minutes showed the lowest a of 0.73 dB/mm/MHz with an acoustic impedance (AI= sound speed (c) x density (rho)) of 1.43 times 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">6</sup> kg/m <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> s at 37degC. Moreover, simulation results reveal that a 5 MHz linear probe using the HTV silicone rubber doped with Yb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> powder showed relative sensitivity around 2.6 dB higher than that in the case of using the RTV silicone rubber doped with Yb <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> powder.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.