Abstract
Here, we studied the influence of pre- and post-thermal annealing on the performance of polymer:fullerene bulk heterojunction solar cells using the conventional architecture, comprising a conjugated polymer, namely, poly(3-hexylthiophene-2,5-diyl) (P3HT) and a fullerene derivative [6,6]-phenyl-C60-butyric acid methyl ester (PC60BM) as a photoactive layer. The non-annealed active layer device exhibited a power conversion efficiency of <1 % , which was significantly lower than the pre- and post-annealed devices. To investigate the impact of pre- and post thermal annealing on the natural morphological state of the polymer, regiorandom (P3HT-I) and regioregular (P3HT-II) type P3HT were compared in photoactive layers. In general, P3HT-I is amorphous, whereas P3HT-II is semi-crystalline. Changes in solar cell performance were associated with changes in carrier extraction efficiencies influenced by the annealing conditions. The charge photogeneration processes were investigated using spectroscopic techniques, including electroluminescence, steady-state, and time-resolved photoluminescence spectroscopy. Finally, to explore the morphological changes upon annealing, atomic force microscopy and electroluminescence imaging measurements were performed on films and solar cells, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.