Abstract
The micro and nano-structured amorphous carbon as p-type films prepared from natural palm oil precursor for heterojunction solar cell were presented. Field-emission scanning electron microscopy (FESEM) revealed the micro and nano structured films had particle size in the range of 382 nm to 689 nm and 28 to 34 nm, respectively. The energy-dispersive spectroscopy (EDS) showed the existing of carbon in micro-structured amorphous carbon film and carbon together with boron in nano-structured amorphous carbon film. Solar simulator analysis results showed an open circuit voltage (VOC), current density (JSC), fill-factor(FF) and conversion efficiency (η) of Au/a-C/n-Si/Au were 264.62 mV, 1.50434 mA/cm2, 0.32632, and 0.130154 %, respectively. Meanwhile, the VOC, JSC, FF and η of Au/a-C:B/n-Si/Au solar cell were 271.25 mV, 14.91723 mA/cm2, 0.33582, and 1.542622 %, respectively. The conversion efficiency was increased as the p-type film was in nanostructure form.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOSR Journal of Electrical and Electronics Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.