Antimony selenide (Sb2Se3) is a promising absorber material for thin-film photovoltaics. However, certain areas of fundamental understanding of this material remain incomplete and this presents a barrier to further efficiency gains. In particular, recent studies have highlighted the role of majority carrier type and extrinsic doping in drastically changing the performance of high efficiency devices (Hobson et al 2020 Chem. Mater. 32 2621–30). Herein, Sn-doped Sb2Se3 bulk crystals are shown to exhibit p-type conductivity using Hall effect and hot-probe measurements. The measured conductivities are higher than those achieved through native defects alone, but with a carrier density (up to 7.4 × 1014 cm−3) several orders of magnitude smaller than the quantity of Sn included in the source material. Additionally, a combination of ultraviolet, x-ray and hard x-ray photoemission spectroscopies are employed to obtain a non-destructive depth profile of the valence band maximum, confirming p-type conductivity and indicating a majority carrier type inversion layer at the surface. Finally, these results are supported by density functional theory calculations of the defect formation energies in Sn-doped Sb2Se3, showing a possible limit on the carrier concentration achievable with Sn as a dopant. This study sheds light on the effectiveness of Sn as a p-type dopant in Sb2Se3 and highlights avenues for further optimisation of doped Sb2Se3 for solar energy devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.