Abstract
Oxygen transmissibility, thickness, and water content were measured for three types of collagen shields: six of each type designed to dissolve in 12, 24, and 72 hours. Oxygen transmissibility was measured by a polarographic method at 35 degrees C and was found to be 17.9, 17.3, and 23.8 x 10(-9) cm mL O2/s mL mm Hg, respectively. Thicknesses were measured with an electronic gauge, and the central thicknesses of the 12-hour shields were found to be significantly greater (mean thickness, 0.19 mm) than the central thicknesses of the other two types (0.15 mm each). Water content, as measured by a hand refractometer, was found to be about 63% for all three types of shields, and no statistically significant differences were found. These measurements indicate that collagen shields behave like 63% water-content hydrogel contact lenses (oxygen permeability estimated at 27 x 10(-11) cm2 mL O2/s mL mm Hg) with regard to oxygen transmission.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.