Abstract
Supportless platinum nanotubes (PtNTs) were synthesized by the decomposition of platinum acetylacetonate vapor within anodic alumina templates at 210°C. As synthesized, the nanotubes are nanoparticulate aggregates composed of Pt crystallites approximately 3 nm in diameter and with a range of lengths from 1 μm to 20 μm. Annealing treatments result in crystallite growth and morphological evolution of the tubular nanostructures including the development of nanoscale porosity. In rotating disk electrode measurements carried out in 0.1 M HClO4, porous PtNTs annealed at 500°C exhibited a specific activity for oxygen reduction of 2390 ± 423 μA/cm2Pt at 0.9 V, comparable to bulk polycrystalline Pt. The electrochemical surface area of the annealed structures was a relatively low 10 m2/g, resulting in a moderate overall mass activity of 240 ± 41 mA/mgPt.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.