Abstract
An asymmetric membrane consisted of a thin functional layer and a thick support was developed for oxygen production and membrane reactors. The functional La 0.8 Sr 0.2 Cr 0.5 Fe 0.5 O 3− δ (LSCrF)–Zr 0.8 Y 0.2 O 2− δ (YSZ) layer was prepared by screen printing and the YSZ support by phase inversion tape casting. Performance of the membrane was evaluated under air/argon, air/CO and CO 2 /H 2 gradient at 750–900 °C. The results indicate the membrane to have good chemical stability and considerable high oxygen permeability under stringent conditions. An oxygen permeation flux of 0.058, 0.175 and 1.198 ml (STP) cm −2 min −1 was obtained at 900 °C for operation under air/argon, CO 2 /H 2 and air/CO gradient, respectively. The apparent activation energy for oxygen permeation was 131.22±19.74, 89.53±6.29 and 66.28±1.41 kJ/mol under air/argon, air/CO and CO 2 /H 2 gradient respectively. The results suggest the membrane to have potential applications in the chemical reactor.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.