Abstract
Increasing the difference of the Ln3+ and A2+ cation radii in perovskite-type Ln0.5A0.5FeO3−δ (Ln = La, Pr, Nd, Sm; A = Sr, Ba) results in higher oxygen deficiency and lower oxygen-ionic and p-type electronic conductivities, determined using the oxygen permeation and total conductivity measurements at 973−1223 K. The relationships between the anion transport and A-site cation size mismatch remain essentially similar in air and under reducing conditions when most iron cations become trivalent, thus confirming critical influence of oxygen-vacancy trapping processes induced by the lattice strain. At low temperatures, analogous correlation is also observed for quadrupole splittings derived from the Mössbauer spectra of oxygen-stoichiometric Ln0.5A0.5FeO3. Contrary to the ionic conductivity variations, the role of surface exchange kinetics as a permeation-limiting factor, evaluated from the membrane thickness dependence of oxygen fluxes, tends to decrease on Ba2+ doping and on decreasing Ln3+ size in Ln0.5Sr0.5FeO3−δ series. The n-type electronic conduction and low-p(O2) stability at 1223 K are substantially unaffected by the cation radius mismatch.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.