Abstract
Measurements of the oxygen diffusivity of ceramic samples of the mixed ionic electronic conductor La0.6Sr0.4Co0.2Fe0.8O3−δ (LSCF6428) have shown the appearance of grain boundary tails in diffusion profiles at temperatures below 600 °C. Analysis of the tails yields values of the grain boundary diffusion products (). The activation enthalpies for the grain boundary and lattice diffusion are very close at 1.69 eV and 1.61 eV respectively, suggesting a common diffusion mechanism. Comparison with literature values on both lattice and grain boundary diffusion products have shown that values of obtained for LSCF6428 are the highest yet recorded for any oxide material. The reasons for this high value are discussed, including the degree of nonstoichiometry of the parent lattice and the possible involvement of the twin boundaries found in these ceramic samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.