Abstract
This study aims at modifying the surface bioactivity of NiTi by sodium and oxygen plasma immersion ion implantation (PIII). Sodium ions were implanted into oxygen plasma-implanted NiTi and untreated NiTi. X-ray photoelectron spectroscopy (XPS) revealed that more sodium was implanted into the oxygen pre-implanted sample in comparison with the untreated surface. Scanning electron microscopy (SEM) coupled with energy dispersive X-ray analysis (EDX) detected calcium and phosphorus rich deposits on both samples after immersion in simulated body fluids for 7 and 21 days. Inductively-coupled plasma mass spectrometry (ICPMS) conducted on the deposits dissolved in diluted hydrochloric acid showed more calcium on the oxygen PIII samples. The improved corrosion resistance of the oxygen PIII NiTi was retained after sodium PIII as evaluated by potentiodynamic polarization tests. Better spreading and proliferation of osteoblasts were also observed on the treated samples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.