AbstractFerroelectric PbZr0.2Ti0.8O3/YBa2Cu3O7 heterostructures have been grown on single crystal LaAIO3 and on buffered [100] Si. The cuprate superconductors are used as metal-like bottom electrodes for the subsequent growth of the ferroelectric PZT thin film. Structural studies using x-ray diffraction, and transmission electron microscopy show that the PZT layer is free of large angle grain boundaries (i.e., single crystal-like). Rutherford backscattering studies reveal the composition of the PZT layer to be close to that of the target. Ferroelectric hysteresis measurements using both pulsed measurements and a variable frequency Sawyer-Tower circuit yield remnant polarization values (at 5V) in the range of 15-45μC/cm2 (depending on deposition conditions) with a coercive field in the range of 80-120kV/cm. At a cycling voltage of 5V, these heterostructures exhibit a fatigue lifetime of better than 2x1010 at 40kHz (the polarization decays by only 20% of the initial value). Pulsed poling experiments before and after show that the loss of polarization is reversible. These heterostructures also show excellent aging and logic state retention characteristics.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.