Abstract
The formation of an ultra-thin aluminum oxide film at Fe0.85Al0.15(110) surface (A2 random alloy) has been studied by a variety of surface sensitive techniques (X-ray photoemission, low-energy electron diffraction, surface X-ray diffraction and scanning tunneling microscopy) supplemented by ab initio atomistic simulations. Since iron is not oxidized in the used conditions, the study focused on the coupling between aluminum oxidation and segregation processes. Compared to the bare surface, whose average composition (Fe0.6Al0.4) is closer to the B2-CsCl structure over a ∼ 3 nm depth, the oxidation hardly affects the subsurface segregation of aluminum. All the structural and chemical fingerprints point to an oxide film similar to that found on NiAl(110). It is a bilayer (∼ 7.5A thick) with a composition close to Al10O13 and a large (18.8 × 10.7)A 2 nearly rectangular unit cell; an almost perfect match between substrate periodicity and the (1 × 2) oxide supercell is found. Nevertheless, microscopy reveals the presence of anti-phase domain boundaries. Measured Al 2p and O 1s core level shifts match calculated ones; their origin and the relative contributions of initial/final state effects are discussed. The ubiquity of the present oxide on different supports asks for the origin of its stability.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.