Abstract
Oxidation process of polycrystalline InN films were investigated using in situ X-ray diffraction (XRD) and X-ray photoemission spectroscopy (XPS). The films were grown by dc sputter on sapphire (0001) substrates and were oxidized in air at elevated temperatures. The XRD data showed that the structure of the films changed to the bixbyite In 2O 3 ( a = 10.11 Å) above 450 °C. Chemical configurations of the sample surfaces were investigated using high-resolution XPS. For the non-intentionally oxidized InN film, XPS analysis on the In 3d peak and the N 1s main peak at 396.4 eV suggests that indium and nitrogen are bound dominantly in the form of InN. An additional peak observed at 397.4 eV in the N 1s photoelectrons and the O 1s peaks indicate that the InN film surface is partly oxidized to have InO x N y configuration. After oxidation of the InN film at elevated temperature, the O 1s spectrum is dominated by In 2O 3 peak, which indicates that the structure is stable chemically with In 2O 3 configuration at least within the XPS probing depth of a few nm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.