Abstract
A displacement-deposited Ag layer was investigated as an oxidation barrier in damascene Cu structure for high performance interconnection. A 40 nm thick bright and continuous Ag film was formed at the surface of electrodeposited Cu by immersing the copper film into the silver displacement solution. The Ag film at Cu surface significantly blocked oxygen diffusion into the Cu film and retarded oxidation. More importantly, an elevated barrier performance for oxygen diffusion through elimination and stuffing of grain boundaries of Cu was observed upon annealing in a 400°C N 2 atmosphere. Outward Cu diffusion through Ag layer controlled Cu oxidation when the surface was passivated with Ag layer.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.