Abstract
In order to further improve the oxidation protective ability of (ZrB2–SiC)/SiC coated graphite, ferrocene was introduced into the outer ZrB2–SiC coatings during pack cementation process. The ferrocene addition increased the porosity of the outer ZrB2–SiC coatings, which was favorable to thermal shock resistance of (ZrB2–SiC)/SiC coated specimens. The ZrB2–SiC coating with 3wt% ferrocene (ZS50-3f) has optimum oxidation protective ability. Its weight retention after 15 thermal shock cycles between 1500°C and room temperature was 96. 2%. The weight loss of ZS50-3f was only 0.2% after 19h oxidation at 1500°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.