Abstract
The oxidation resistance of 18%Cr-oxide dispersion strengthened (ODS) ferritic steels with and without 5%Al has been investigated in air at 700900 °C for time period up to 540 h. The oxidation rate of ODS steels is significantly dependent on the oxidation time and temperature. Compared to Al-containing ODS steel, the finer grains of Al-free ODS steel are due to the formation of smaller coherent oxide particles which suppress the steel's grain growth. The grain refinement of ODS steels is expected to allow rapid segregation of Cr or Al to the steel surface, so that the continuous Fe-Cr spinel or alumina layer is formed quickly in comparison to the alloys without oxide particles dispersion. Therefore, the excellent oxidation resistance of ODS steels is owing to the formation of continuous, protective oxide layers which correlate with oxide nanoparticles and grain refinement.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.