Abstract
In this article, the high‐temperature (≥1000 °C) oxidation kinetics of porous magnesium‐manganese oxide structures considered for large‐scale thermochemical energy storage are determined. For this analysis, oxides with Mn/Mg molar ratios of 2/3, 1/1, and 2/1 are synthesized via solid‐state reaction and crushed to a powder with particle sizes ranging from 125 to 180 μm. The powder is thermally reduced at 1500 °C inside a heated alumina tube under argon flow. Subsequently, the resulting porous bed is oxidized at temperatures between 1000 and 1500 °C with an oxygen to argon molar ratio of 1:4 (leading to an oxygen partial pressure of 0.2 atm). An Arrhenius‐type kinetic rate law is derived using the theory of internal oxidation assuming spherical particles. Subsequently, the kinetic rate law parameters are identified by comparing measured oxygen flow at the reactor outlet to the oxygen output computed using a 1D plug flow reactor model incorporating the postulated kinetic model. Results indicate that the derived bulk kinetic rate law describes the measured oxidation kinetics well and is suited for designing thermochemical energy storage modules based on magnesium‐manganese oxides.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.