Abstract
In this work, we investigate the microstructure and oxidation of Si nanopillars and report that the oxidation at the sidewall of Si pillars is initially retarded (the so-called self-limiting) and eventually stops altogether at a certain size (stopping size), and further oxidation causes cracks at the bottom of the pillars, that depends on the initial Si nanopillar diameter and the experimental conditions. The diffusion of oxidant in the oxide and the compressive stress due to volume expansion from Si to SiO2 caused by the old oxide are insufficient to explain the above phenomenon. Herein, the chemical reaction (breaking of Si–Si bonds) that causes the remaining Si–Si bonds to shrink is introduced; this new model well explains the oxidation of Si nanopillars with the evidence of the change in crystal planes distances observed from transmission electron microscope. The present work contributes to the intrinsic understanding and precise controlling of oxidation in Si nanopillars for future device fabrication.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.