Abstract
ABSTRACTSevere oxidation inhibited epitaxy when buried Sb profiles in single crystal silicon were formed from evaporated layers irradiated in atmosphere with a pulsed Q-switched ruby laser. Oxygen concentrations as high as 5×1017atoms/cm2 (equivalent to 105nm SiO2) were measured. However, structures prepared without the Sb layer and irradiated under identical conditions, showed no oxidation. Oxidation of Sb as a source of the measured oxygen was ruled out, while the total heating time during laser irradiation is so short (nano- to milliseconds) that normal oxidation kinetics cannot account for the amount of SiO2 measured. Irradiations in vacuum and in a helium ambient showed that the oxygen responsible for these effects is supplied from the ambient in which irradiations are carried out. Also no oxidation was observed when structures, prepared on a substrate heated to 350°C, were irradiated in atmosphere. A model to account for these oxidation effects is proposed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.