Abstract
Ni/8 mol% Y2O3-stabilized zirconia cermets are used in thin-film electrolyte solid-oxide fuel cells as support substrates. Rapid oxidation of the metallic Ni can cause failure of the substrate and of the whole system. The rate of Ni oxidation in air and in an inert atmosphere containing water vapor was determined as a function of temperature between 500 and 950 °C. A logarithmic rate law describes the oxidation kinetics in air, whereas a linear rate law fits the first branch of the curve of the experimental data in a humidified inert atmosphere. The substrate exhibits no significant mechanical degradation after uniform oxidation under moderate conditions. However, the observed bending of the samples after oxidation in humidified argon, due to the nonuniform oxidation, can cause damage to fuel cell
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.