Abstract
Fatigue strength and life of weldment at high temperatures are important for the materials in power plants. The fatigue crack growth rate is accelerated by oxidation. Similarly, the high-temperature fatigue life is influenced by oxidation. The base metal, the weld metal and the heat-affected zone (HAZ) of the P122 (Cr–Mo steel) weldment were oxidized between 600 °C and 700 °C for up to 500 h in air, and their oxidation behavior was examined. The oxidation resistance increased in the order of HAZ, base metal and weld metal. The scales were mainly Fe 2O 3. Fatigue tests were performed to measure the fatigue crack growth rate in the range of low stress intensity factor, and the results are discussed from the viewpoint of different microstructures and oxidation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.